Sensory and physical properties of 2 lemon-flavored beverages with 5% and 7.5% wt/wt nonfat dry milk (NFDM) at pH 2.5 were studied during storage. The 2 beverages had similar volatile compounds, but the 5% NFDM had higher aroma and lemon flavor, with a preferred appearance by consumers due to the lower turbidity and viscosity. After 28 d of storage at 4°C, lemon flavor decreased in the 5% NFDM beverage but was still more intense than the 7.5% one. During 70 d of storage, no microorganisms were detected, and the beverages were more stable when stored at 4°C than at room temperature according to changes of physical properties measured for appearance, turbidity, color, particle size, zeta potential, rheological properties, and transmission electron microscopy morphology. Findings of the present study suggest that NFDM may be used at 5% wt/wt to produce stable acidic dairy beverages with low turbidity when stored at 4°C.     

基于蜻蜓翅脉结构的连续碳纤维增强树脂基复合材料仿生设计与增材制造

以具有轻质高强优异性能的蜻蜓翅脉结构为设计灵感，在分析翅脉网格结构抗冲击原理的基础上，设计了传统和仿生两类对比结构。采用熔融挤出3D打印机成功制备了具有不同结构的连续碳纤维增强聚乳酸复合材料试样，并对不同结构复合材料试样的拉伸性能和抗冲击性能进行了测试和对比分析。研究分析结果表明：由于拉伸力方向上的连续碳纤维含量相对较少，限制了仿生结构复合材料抗拉强度的提高，但仿生结构的平均抗拉强度为传统结构的1.18倍；当仿生结构复合材料试样受到冲击力时，其内部六边形结构的连接角度会发生变化，从而极大消耗冲击能量，同时具有六边形网格结构的连续碳纤维可以有效阻碍裂纹的扩展，因此仿生结构的平均冲击韧性可以达到传统结构的2.46倍；仿生蜻蜓翅脉结构可以显著提高增材制造复合材料的综合力学性能，且对于抗冲击性能的提高具体突出效果。连续碳纤维增强树脂基复合材料的有效可行的仿生蜻蜓翅脉结构设计和增材制造，可极大扩展其在高冲击载荷领域中的相应应用。     

Porous agarose/Gd-hydroxyapatite composite bone fillers with promoted osteogenesis and antibacterial activity

Artificial bone fillers are essentially required for repairing bone defects, and developing the fillers with synergistic biocompatibility and anti-bacterial activity persists as one of the critical challenges. In this work, a new agarose/gadolinium-doped hydroxyapatite filler with three-dimensional porous structures was fabricated. For the composite filler, agarose provides three-dimensional skeleton and endows porosity, workability, and high specific surface area, hydroxyapatite (HA) offers the biocompatibility, and the rare earth element gadolinium (Gd) acts as the antibacterial agent. X-ray photoelectron spectroscopy detection showed the doping of Gd in HA lattice with the formation of Gd-HA interstitial solid solution. Attenuated total reflection Fourier transform infrared spectroscopy imaging suggested chemical interactions between agarose and Gd-HA, and the physical structure of agarose was tuned by the Gd-doped HA. Cytotoxicity testing and alizarin red staining experiments using mouse pro-osteoblasts (MC3T3-E1) revealed remarkable bioactivity and osteogenic properties of the composite fillers, and proliferation and growth rates of the cells increased in proportion to Gd content in the composites. Antibacterial testing using the gram-positive bacteria S. aureus and the gram-negative bacteria E. coli indicated promising antibacterial properties of the fillers. Meanwhile, the antibacterial properties of composite filles were enhanced with the increase of Gd content. The antibacterial fillers with porous structure and excellent physicomechanical properties show inspiring potential for bone defect repair.     

Nanofiber structured oxygen defective CoFe2O4-x catalyst for the water-gas shift reaction in waste-to-hydrogen processes

Waste-to-hydrogen processes are a way to produce hydrogen from waste and reduce the amount of landfill/incineration of wastes simultaneously through the gasification of waste. The water-gas shift (WGS) reaction is a key step in this waste-to-hydrogen process by removing the CO and producing additional H₂. A nanofiber-structured CoFe₂O₄ catalyst was synthesized by the electrospinning method, and the catalytic performance in WGS using waste-derived synthesis gas was compared with that of catalysts prepared by sol-gel, hydrothermal, and co-precipitation methods. The CoFe₂O₄ catalyst synthesized by the electrospinning method showed a clear nanofiber structure and revealed a superior redox property. This superior redox property, which has a large relation with the high oxygen storage capacity of the catalyst, induced the formation of an active phase (Co⁰ and Fe₃O₄) in CoFe₂O₄. As a result, the nanofiber structured oxygen defective CoFe₂O_4-x prepared by the electrospinning method showed the best catalytic activity in this study.     

Facile self-assembly approach to construct a novel MXene-decorated nano-sized phase change material emulsion for thermal energy storage

In recent years, phase change material emulsions (PCMEs) with enhanced energy storage capacities and good flow characteristics have drawn significant attention. However, due to the thermodynamically unstable nature and tiny particle confinement, the nanomaterial modification strategies at PCM/water interface to improve stabilities and reduce supercooling of nano-sized PCMEs (NPCMEs) are very limited and challenging. Herein, we report a facile strategy for constructing MXene-decorated NPCME with good stability, little supercooling, and high thermal conductivity by self-assembly of MXene nanosheets at PCM/water interface. The concentrations of MXene have great influences on the average droplet diameters, stabilities, and thermophysical properties of the NPCMEs. The results show that the PCMs have been well dispersed into the water in the form of quasi-spherical droplets, with average droplet diameters of 242–805 nm. The thermal conductivity of 10 wt% n-tetradecane/water NPCME containing 9 mg ml^-1 MXene is 0.693 W m^-1·K^-1, achieving an enhancement by 15.5%, as compared to that of water. Besides, the MXene-decorated paraffin/water NPCMEs exhibit little supercooling and enhanced heat storage capacities. More importantly, this facile self-assembly strategy opens a new platform for preparing high-performance NPCMEs, which can be used as novel heat transfer fluids for thermal energy storage systems.     

Preparation and properties of AZO/PS/AZO tri-layer transparent conductive film with a light-trapping structure

The light-trapping structure is an effective method to increase solar light capture efficiency in the solar cells. In this study, Al-doped ZnO (AZO)/polystyrene (PS)/AZO tri-layer transparent conductive film with light-trapping structure was fabricated by magnetron sputtering and liquid phase methods. The structural, optical and electrical properties of the AZO films could be controlled by different growth conditions. When the sputtering pressure of the under-layer AZO film was 0.2 Pa, the discharge voltage was around 80 V, which was within the optimal process window for obtaining AZO film with high crystallinity. The optimal under-layer AZO film had a large surface roughness and a very low static water contact angle of 75.71°, promoting the relatively uniform distribution of PS spheres. Under this sputtering condition, the prepared AZO/PS/AZO tri-layer film had the highest crystallinity and least point defects. The highest carrier concentration and Hall mobility are 3.0 × 10²¹ cm^-3and 5.39 cm² V^-1 s^-1, respectively. Additionally, a transparent conductive film with the lowest resistivity value (3.88 × 10^-4 Ω cm) and the highest average haze value (26.5%) was obtained by optimizing the process parameters. These properties were comparable to or exceed the reported values of surface-textured SnO₂-based as well as ZnO-based TCOs films, making our films suitable for transparent electrode applications, especially in thin-film solar cells.     

Effects of non-thermal plasma treating wheat kernel on the physicochemical properties of wheat flour and the quality of fresh wet noodles

The effects of non-thermal plasma (NTP) on the physicochemical properties of wheat flour and the quality of fresh wet noodles ( FWN) were investigated. The results showed that NTP effectively decreased the total plate count (TPC), yeast and mould count (YMC) and Bacillus spp. in wheat flour. Wet gluten contents and the stability time reached the maximum when treated for 20 s. The viscosity of starch increased significantly after treatment due to the increased of damaged starch. The contents of secondary structure were altered to some extent, which was because that the ordered network structure of gluten protein broken. Furthermore, compared with the control, texture properties of FWN were enhanced significantly at 20 s, and the darkening rate of FWN was greatly inhibited due to the low polyphenol oxidase (PPO) activity. Consequently, the most suitable treatment was 500 W for 20 s, providing a basis for the application of NTP in flour products.     

Mathematical law of size effect on the flexural property of ceramics

Brittle materials generally exhibit size effects, and the mechanical properties of these materials degrade significantly with an increase in size. However, the mathematical law governing the attenuation degree of mechanical properties with the increase in size is still unknown. In this study, maximum loads of differently sized ceramic test strips were subjected to three point bending tests under two working conditions of equal spans and span amplifications, respectively. Subsequently, the theoretical maximum loads of materials were calculated using the finite element method (FEM). By calculating the difference between the calculated values and the actual maximum loads, the attenuation of mechanical properties of ceramic samples were observed. The results show that the theoretical mechanical properties and the performance attenuation caused by the size effect tend to increase according to the following equation: y=ax³+bx²+cx+d. Therefore, mechanical properties and performance attenuation of any sample exhibiting a size within the experimental range can be predicted by a mathematical law, which was obtained through mechanical tests results of four samples with different sizes. The obtained mathematical law holds great significance for predicting the mechanical properties of materials under size effects.     

Novel Bi4O5Br2/MnxZn1-xFe2O4 magnetic composite with an enhanced photodegradation activity and excellent recyclability

Bi₄O₅Br₂/Mn_xZn_1-xFe₂O₄ nanocomposites with impressive photocatalytic and recyclability properties were synthesised using a microemulsion method. In addition to the photocatalytic effect, the crystal structure and morphology, photoelectrochemical characteristics, magnetic effect and photocatalytic mechanism of Bi₄O₅Br₂/Mn_xZn_1-xFe₂O₄ were also investigated. As the best sample, the removal rate of the Bi₄O₅Br₂/Mn_xZn_1-xFe₂O₄ photocatalyst with 7.5 wt% Mn_xZn_1-xFe₂O₄ to rhodamine B (RhB) reached up to 99.4% within 60 min. The enhanced photocatalyst activity was mainly attributed to the type-II heterojunction formed between Bi₄O₅Br₂ and Mn_xZn_1-xFe₂O₄, which not only optimised the energy band structure, but also led to the building of an interior electromagnetic field within the Bi₄O₅Br₂/Mn_xZn_1-xFe₂O₄ heterojunction. Meanwhile, the constantly producing and migrating h⁺ and ·O₂^? were the main active components. In particular, the results of the saturation magnetization tests and magnetic recovery experiments revealed that the magnetic composite photocatalyst can be recovered effectively. The results of the removal rate of RhB remaining at 85.2% after five uses reflected the advantages of the stability of the Bi₄O₅Br₂/Mn_xZn_1-xFe₂O₄ photocatalyst. In brief, this paper presented an original idea to develop a novel composite magnetic photocatalyst and research the enhancement mechanism of photocatalysis.     

Achieving superior hydrogen storage properties via in-situ formed nanostructures: A high-capacity Mg–Ni alloy with La microalloying

Mg-based hydride is a promising hydrogen storage material, but its capacity is hindered by the kinetic properties. In this study, Mg–Mg₂Ni–LaH_x nanocomposite is formed from the H-induced decomposition of Mg₉₈Ni_1·67La_0.33 alloy. The hydrogen capacity of 7.19 wt % is reached at 325 °C under 3 MPa H₂, attributed to the ultrahigh hydrogenation capacity in Stage I. The hydrogen capacity of 5.59 wt % is achieved at 175 °C under 1 MPa H₂. The apparent activation energies for hydrogen absorption and desorption are calculated as 57.99 and 107.26 kJ/mol, which are owing to the modified microstructure with LaH_x and Mg₂Ni nanophases embedding in eutectic, and tubular nanostructure adjacent to eutectic. The LaH_2.49 nanophase can catalyze H₂ molecules to dissociate and H atoms to permeate due to its stronger affinity with H atoms. The interfaces of these nanophases provide preferential nucleation sites and alleviate the “blocking effect” together with tubular nanostructure by providing H atoms diffusion paths after the impingement of MgH₂ colonies. Therefore, the superior hydrogenation properties are achieved because of the rapid absorption process of Stage I. The efficient synthesis of nano-catalysts and corresponding mechanisms for improving hydrogen storage properties have important reference to related researches.